MIROTHANE PU 5610 Pigmented Topcoat

Code: 5610

High performance, two pack, acrylic modified polyurethane coating. MIROTHANE PU 5610 has superior adhesion over a wide variety of substrates.

Features

Features

  • Outstanding durability, gloss and colour retention
  • Excellent opacity, achieve a high gloss finish with minimal coats

Specifications

Specifications

Colour : White and Tinted Colours
Finish : Gloss
Build : Good
Sandability : Good
Vertical Hold Up : Good
Solvent Resistance : Excellent
Water Resistance : Excellent
Levelling & Flow : Excellent
Sink Back : Minimal
Coverage : 6m2 per litre at 150 micron wet film build. This is dependent on the application equipment / gun set up and the article being coated
Dry Time : Refer to Technical Data Sheet
Clean Up : Clean all equipment using MIROSOL 1222 or 1286 Thinner

 

Tech Data Sheet

Application

Application

Mix Ratio (by volume) : 4 Parts 5610 Part A + 1 Part 5789 Part B (4A: 1B).
Pot Life : Up to 10 hours Pot life varies significantly with ambient temperature, humidity and the quantity mixed. Pot life is longer at lower temperatures and shorter at higher temperatures. The larger the quantity mixed, the shorter the pot life will be. Only mix the quantity required for the job.
Thinning : 25-40% with MIROSOL 1266 (fast), 1260 (Medium), 1218 (Slow) thinner.

 

Suction Gun - Use 1.5 to 2mm (59-79 thou) orifice with 350-400kpa (50-55 psi).
Pressure Pot - Use 1.5 to 2mm (59-79 thou) orifice with pressure pot air-cap. Gun pressure 350-400kpa (50-55 psi) and a pot pressure of 45kpa (6 psi) max.
Airless Spray - Use 0.23 to 0.33mm (9-13 thou) orifice, 15cm fan (dependent on job) with regulated pump pressure of 350-400kpa (50-55 psi).
Air Mix Guns - Settings similar to airless spray with the air-assisted regulator pressure at 70-90kpa (10-15psi).

Where to Use

Where to Use

Petrochemical industry, road tankers, tank farms, marine environment, concrete mixing bowls, trailers, horse floats, truck chassis, automotive, CFC toilet partitions.